Two-metal tab tape, double-sided csp tape, bga tape and method for manufacturing the same

ABSTRACT

A two-metal TAB tape, double-sided CSP tape, and BGA tape in which the tape has an insulating substrate and wiring layers at least on both sides of the insulating substrate, sprocket holes are made at regular intervals in the longitudinal direction along the edges in the direction of the width, through holes are made in the substrate by punching press, the through holes are filled with conductor by punching press, and the conductor is electrically connected to the wiring layers, characterized in that pilot round holes are made among the sprocket holes made in the longitudinal direction. Methods for producing such two-metal TAB tape, double-sided CSP tape, and BGA tape are disclosed.

TECHNICAL FIELD

[0001] This invention relates to a 2-metal layer TAB tape and a both-sided CSP•BGA tape, and a process of producing them.

BACKGROUND ART

[0002] Various types of wiring boards having a conductor layer on both sides thereof are in use. Such wiring boards include those using a flexible substrate, e.g., polyimide, such as a TAB (tape automated bonding) tape, a CSP (chip size package), a BGA (ball grid array), and an FPC (flexible printed circuit); and so-called multilayer printed wiring boards using a rigid substrate, e.g., a glass epoxy laminate.

[0003] A substrate having a conductor layer on both sides thereof is produced by making sprocket holes along the both width direction edges of a substrate in the longitudinal direction at regular pitches by a punching press. Sometimes through-holes, etc. are also made by this punching press.

[0004] Thereafter a wiring layer is formed on both sides of the substrate by etching and the like. Through-holes are then made in the substrate by means of a punching machine. The through-holes are filled with a conductor by a punching (implanting) process, followed by forming a finish plating layer.

[0005] In forming the wiring layer by an etching process, the tape is transported by employing the sprocket holes. The sprocket holes are also available as the pilot holes for registration in filling the through-holes with a conductor (implanting process).

[0006] However, there are some cases that slight deformation of the sprocket holes takes place during a wiring layer formation process. By using the deformed sprocket holes as the registration hole for the implanting process, the registration accuracy becomes worse. Further, since the sprocket holes are rectangular, a slight shift occurs when the deformed sprocket holes are used as pilot holes, which also results in that the registration accuracy becomes worse in the implanting process. The inaccuracy of registration has given rise to the fluctuation of the properties of products by lot-by-lot manufacturing when they are transferred to a mass production stage.

DISCLOSURE OF THE INVENTION

[0007] Accordingly, an object of the present invention is to provide 2-metal layer TAB and both-sided CSP•BGA tapes and to provide a process of producing the tapes which do not have any fluctuation of the properties of products, even when they are produced in a mass production system.

[0008] As a result of investigation, the present inventors have found that the above object is accomplished by making round holes between sprocket holes which are used as pilot holes in filling through-holes with a conductor by means of a punching press.

[0009] The present invention has been completed based on the above finding. The present invention provides a 2-metal layer TAB or both-sided CSP•BGA tape having an insulating substrate and a wiring layer provided on at least both sides of the substrate, the substrate having evenly spaced sprocket holes on both width direction edges in the longitudinal direction thereof and also having through-holes formed with a punching press, and the through-holes being filled with a conductor by means of a punching press such that the conductor and the wiring layers are electrically connected, which is characterized by having round pilot holes between the sprocket holes formed in the longitudinal direction thereof.

[0010] The present invention also provides a process of producing a 2-metal layer TAB or both-sided CSP•BGA tape which comprises forming sprocket holes and round pilot holes along both width direction edges of an insulating substrate in the longitudinal direction thereof alternately and at regular pitches by a punching press, forming a wiring layer or a metal foil on at least both sides of the substrate, forming through-holes with a punching press, and filling the through-holes with a conductor with a punching press to electrically connect the conductor to the wiring layers or the metal foils.

BRIEF DESCRIPTION OF THE DRAWINGS

[0011]FIG. 1 is a plan view of an example of the 2-metal layer TAB tape according to the present invention.

[0012]FIG. 2 is a block diagram showing an example of the process of producing the 2-metal layer TAB tape according to the present invention.

[0013]FIG. 3 is an illustration showing the method of measuring a maximum shift of pattern position accuracy in Example 1 and Comparative Example 1.

BEST MODE FOR CARRYING OUT THE INVENTION

[0014] The embodiments for carrying out the present invention are described below.

[0015] Two metal layer TAB and both-sided CSP•BGA tapes and a process of producing them are discussed first. While the present invention is widely applicable to flexible substrates, e.g., polyimide, such as TAB tapes, CSPs, BGAs and FPCs, and so-called multilayer printed wiring boards using a rigid substrate such as a glass epoxy laminate as stated above, the following chiefly refers to application to TAB tapes, particularly what we call 2-metal layer TAB tapes having a wiring layer on both sides and a process of making them.

[0016]FIG. 1 is a plan view showing an example of the 2-metal layer TAB tape according to the present invention. In FIG. 1, numeral 1 indicates a 2-metal layer TAB tape; 2, an insulating substrate; 3, a wiring layer; 4, sprocket holes; and 5, round pilot holes.

[0017] As shown in FIG. 1, the 2-metal layer TAB tape 1 of the present invention has a wiring layer 3 formed on the surfaces of the insulating substrate 2. A polyimide film is usually used as the insulating substrate 2. The wiring layer 3 is formed by, for example, etching a copper foil, etc.

[0018] The 2-metal layer TAB tape 1 has evenly spaced sprocket holes 4 along both edges of the width direction thereof in the longitudinal direction thereof. Round pilot holes 5 are made between the sprocket holes 4 made in the longitudinal direction. The sprocket holes 4 and the round pilot holes 5 are formed by the punching press. The sprocket holes 4 have a square shape and are used to carry the tape in forming the wiring layers 3. On the other hand, the round pilot holes 5 are used as a guide for a mold in the implanting process a conductor to form a through-hole conductor layer. The round pilot holes 5 have a diameter of about 1 mm. Not used for tape transportation, the round pilot holes keep their shape without undergoing wear or deformation. Being round-shaped, the pilot holes 5 allow columnar pilot pins to be fitted therein exactly, causing no shift in positioning.

[0019] The 2-metal layer TAB tape of the present invention has through-holes formed by means of a punching press, in which a conductor is implanted by means of a punching press to make electrical connections between the conductor and the above-mentioned wiring layers.

[0020] The process of producing the 2-metal layer TAB is then described. FIG. 2 is a block diagram showing an example of the process for producing the 2-metal layer TAB tape of the present invention. As shown in FIG. 2, a polyimide tape cladded with copper on both sides is press-punched to form sprocket holes and round pilot holes. Through-holes, etc. are also formed in some cases. The sprocket holes are rectangular while the round pilot holes are circular. The round holes have a diameter of about 1 mm.

[0021] After the copper surface is subjected to pretreatment (pickling and degreasing), a photoresist is applied thereto. A wiring layer is formed by exposure, development, and etching. In the same manner, the backside is subjected to pretreatment (pickling and degreasing), a photoresist is applied thereto, and a wiring layer is formed by exposure, development and etching.

[0022] When the both-sided laminate substrate having a photoresist thereon is imagewise exposed to ultraviolet light by means of a pattern exposure system, sprocket pins (guide pins) provided on the stage of the pattern exposure system fit into the sprocket holes of the tape to transport the tape. While the tape is transported in this way, the sprocket holes sometimes undergo deformation. The sprocket holes generally have a square shape with a side length of 1.981 mm or 1.42 mm.

[0023] Finally, through-holes are made with a punching press, and a conductor is implanted into the through-holes with a punching press to electrically connect the conductor and the wiring layers or the metal foils. Finish plating, such as nickel/gold plating, is conducted to improve reliability of the electrical connections to obtain a final product.

[0024] In the present invention, through-holes are formed by the punching press as described above, so that desmearing as in a wet process is not needed. Electrical connections are also achieved by a punching method using an ordinary punching press. That is, a conductor, such as a solder plate or a copper foil, is put on the substrate having press-punched holes and again punched to implant the conductor into the holes. This is an extremely simplified step, which leads to cost reduction.

[0025] When a conductor is implanted into the through-holes with a punching press, registration can be effected by fitting pilot pins through the round pilot holes made in the tape. Not used as guide holes for tape transportation in circuit formation, the round pilot holes do not suffer deformation. The pilot holes being round, the pilot pins fit therein neatly.

[0026] Since registration in the implanting process is carried out by the use of the round pilot holes which, not used as guide holes for tape transportation, do not suffer deformation and into which round pilot pins fit neatly, registration is accurate. As a result, fluctuation of properties do not occur even in the mass production.

[0027] As stated, the present invention is widely applicable to TAB tapes, CSPs, BGAs and FPCs which use a flexible substrate such as polyimide, and so-called multilayer printed wiring boards using a rigid substrate such as a glass epoxy laminate.

[0028] The present invention will further be illustrated in greater detail based on Examples.

EXAMPLE 1

[0029] A 2-metal layer TAB tape as shown in Table 1 was produced in accordance with the production steps shown in FIG. 2 by using a 35 mm wide polyimide film cladded with copper on both sides (polyimide layer thickness: 50 μm; copper foil thickness: 18 μm each; trade name: Espanex, produced by Nippon Steel Chemical Co., Ltd.). In the step of punching press shown in FIG. 2, sprocket holes and round pilot holes were formed alternately and at regular pitches. The sprocket holes were used for tape transportation, and the round pilot holes were used for registration in the implanting process.

[0030] As a result, the average resistance was 6 mΩ/hole (diameter: 100 μm) with a standard deviation of 0.3 mΩ/hole.

COMPARATIVE EXAMPLE 1

[0031] A 2-metal layer TAB tape was produced in the same manner as in Example 1, except that only sprocket holes were made in the step of punching press shown in FIG. 2 and that the sprocket holes were used for both tape transportation and registration in the implanting process.

[0032] As a result of four runs of testing, the average resistance in each run was 6 to 8 mΩ/hole (diameter: 100 μm) with a standard deviation of 1 to 6 mΩ/hole.

[0033] The maximum shift of pattern position accuracy in terms of a shift of the center of holes was measured according to the method of FIG. 3. In FIG. 3, X is a tape running direction, and Y is a tape width direction. The maximum shift was represented by the distance in X direction. Measurement was made on 7 points. The results obtained are shown in Table 1. TABLE 1 (μm) Hole Example 1 Comparative Example 1 1 10 50 2 5 65 3 10 55 4 0 60 5 5 85 6 10 75 7 15 70

[0034] As is apparent from the results of Table 1, Example 1 was superior to Comparative Example 1 in pattern position accuracy by about 50 μm in average.

INDUSTRIAL APPLICABILITY

[0035] As described above, the 2-metal layer TAB and both-sided CSP•BGA tapes of the present invention do not show fluctuation of properties even in the mass production. The production process of the present invention provides the 2-metal layer TAB and both-sided CSP•BGA tapes easily and conveniently. 

1. A 2-metal layer TAB and a both-sided CSP•BGA tape having an insulating substrate and a wiring layer provided on at least both sides of the substrate, said substrate having evenly spaced sprocket holes on both width direction edges in the longitudinal direction thereof and also having through-holes formed with a punching press, and said through-holes being filled with a conductor by means of a punching press such that said conductor and said wiring layers are electrically connected, which is characterized by having round pilot holes between said sprocket holes formed in the longitudinal direction thereof.
 2. The 2-metal layer TAB and the both-sided CSP•BGA tape according to claim 1, which has three or more layers inclusive of a metal layer.
 3. The 2-metal layer TAB and the both-sided CSP•BGA tape according to claim 1 or 2, wherein said conductor is a metal.
 4. The 2-metal layer TAB and both-sided CSP•BGA tape according to claim 3, wherein said metal is lead, tin, copper or silver or an alloy mainly comprising these metals.
 5. The 2-metal layer TAB the both-sided CSP•BGA tape according to any one of claims 1 to 4, which is plated with nickel and gold.
 6. A process of producing a 2-metal layer TAB or both-sided CSP•BGA tape which comprises forming sprocket holes and round pilot holes along both width direction edges of an insulating substrate in the longitudinal direction thereof alternately and at regular pitches by a punching press, forming a wiring layer or a metal foil on at least both sides of said substrate, forming through-holes with a punching press, and filling said through-holes with a conductor with a punching press to electrically connect said conductor to said wiring layers or said metal foils.
 7. The process of producing a 2-metal layer TAB or both-sided CSP•BGA tape according to claim 6, which has three or more layers inclusive of a metal layer.
 8. The process of producing a 2-metal layer TAB or both-sided CSP•BGA tape according to claim 6 or 7, wherein said conductor is a metal.
 9. The process of producing a 2-metal layer TAB or both-sided CSP•BGA tape according to claim 8, wherein said metal is lead, tin, copper or silver or an alloy mainly comprising these metals.
 10. The process of producing a 2-metal layer TAB or both-sided CSP•BGA tape according to any one of claims 6 to 9, which is plated with nickel and gold. 